  • NSN0604 Magcraft Packaged
  • NSN0604 Dimensions

NSN0604

Rare-Earth Disc Magnets, 1 in. Diameter x 0.125 in. Thick, 4-Count

Price: $13.99
Shipping:
Calculated at checkout
Bulk Discounts for Rare-Earth Disc Magnets, 1 in. Diameter x 0.125 in. Thick, 4-Count

Below are the available bulk discount rates for each individual item when you purchase a certain amount

  • Buy 10 - 19 and pay only $13.29 each
  • Buy 20 - 59 and pay only $12.94 each
  • Buy 60 or above and pay only $12.59 each
Number of Packages:
  • Specifications

    Product Description

    These disc magnets are 1.000 inch (25.4mm) diameter and 0.125 inch (3.2mm) thick. They are magnetized through the thickness. They are composed of grade 40 neodymium iron boron magnetic material and are plated in nickel-copper-nickel for a shiny corrosion resistant finish. Their individual pull force is approximately 10 lbs. Maximum working temperature is 176 F (80 C).

    Part Number NSN0604
    Imperial Dimensions 1 inch diameter x 0.125 inch thick
    Metric Dimensions 25.4mm diameter x 3.175mm thick
    Material Sintered Neodymium-Iron-Boron (NdFeB)
    Shape Disc
    Plating Ni-Cu-Ni (Nickel)
    Magnetization Direction Thickness
    Grade N40
    Pull Force (lbs[g]) 10.69[4849]
    Surface Field(G) 2612
    Maximum Operating Temperature 80 Deg C (176 Deg F)
    Dimensional Tolerance +/-0.005"
    Magnet Quantity 4
    Volume (cm3) 1.61
    Weight (g) 12.07
    Brand Magcraft
    Packaging Magpak Tube
    UPC 875661000047
    Remanent Flux Density Br (kG [T]) 12.5-12.8 [1.25-1.28]
    Coercivity HcB (kOe [kA/m]) >=11.3 [>=923]
    Intrinsic Coercivity HcJ (kOe [kA/m]) >=12.0 [>=995]
    Maximum Energy Product Bhmax (MGOe [kJ/m3]) 38-41 [302-326]
    Density p(g/cm3) >=7.45
    Compression Strength (Mpa) 600-1200
    Bending Strength (Mpa) 150-380
    Vickers Hardness (HV) 460-660
    Recoil Permeability (urec) 1.05
    Electrical Resistance (Ohm*mm2/m) 1.25-1.55
    Curie Temperature Tc (°C) 310
    Thermal Expansion Coefficient 100°C//(x10^-6/K) 6
    Thermal Expansion Coefficient 100°C?(x10^-6/K) -1

    Documents

    RoHS Certificate
    2D CAD Drawing
    Specification Sheet
    IGES CAD File
    STEP CAD File
  • Specifications

    Product Description

    These disc magnets are 1.000 inch (25.4mm) diameter and 0.125 inch (3.2mm) thick. They are magnetized through the thickness. They are composed of grade 40 neodymium iron boron magnetic material and are plated in nickel-copper-nickel for a shiny corrosion resistant finish. Their individual pull force is approximately 10 lbs. Maximum working temperature is 176 F (80 C).

    Part Number NSN0604
    Imperial Dimensions 1 inch diameter x 0.125 inch thick
    Metric Dimensions 25.4mm diameter x 3.175mm thick
    Material Sintered Neodymium-Iron-Boron (NdFeB)
    Shape Disc
    Plating Ni-Cu-Ni (Nickel)
    Magnetization Direction Thickness
    Grade N40
    Pull Force (lbs[g]) 10.69[4849]
    Surface Field(G) 2612
    Maximum Operating Temperature 80 Deg C (176 Deg F)
    Dimensional Tolerance +/-0.005"
    Magnet Quantity 4
    Volume (cm3) 1.61
    Weight (g) 12.07
    Brand Magcraft
    Packaging Magpak Tube
    UPC 875661000047
    Remanent Flux Density Br (kG [T]) 12.5-12.8 [1.25-1.28]
    Coercivity HcB (kOe [kA/m]) >=11.3 [>=923]
    Intrinsic Coercivity HcJ (kOe [kA/m]) >=12.0 [>=995]
    Maximum Energy Product Bhmax (MGOe [kJ/m3]) 38-41 [302-326]
    Density p(g/cm3) >=7.45
    Compression Strength (Mpa) 600-1200
    Bending Strength (Mpa) 150-380
    Vickers Hardness (HV) 460-660
    Recoil Permeability (urec) 1.05
    Electrical Resistance (Ohm*mm2/m) 1.25-1.55
    Curie Temperature Tc (°C) 310
    Thermal Expansion Coefficient 100°C//(x10^-6/K) 6
    Thermal Expansion Coefficient 100°C?(x10^-6/K) -1